SECAR® 70V

SECAR® 70V is a calcium aluminate binder with specially controlled chemistry and mineralogy optimised for conventional castable application of India. SECAR® 70V shows versatility in terms of installation techniques of conventional castables. It develops good flow even at high ambient temperature, making it compatible to Indian climate. Good flow with low water demand makes SECAR® 70V-containing conventional castables suitable for vibration casting application. Moreover, SECAR® 70V-containing patching castables are found to develop an appropriate rheology which helps sticking to the wall. For all types of installations, SECAR® 70V-containing conventional castables show long working time, yet fast hardening leading to a quicker demoulding and rapid return to service.

SECAR® 70V

Frequently asked questions
To know more about Specification and Performance

Typical properties of a castable based on SECAR® 70V

Formulation type
Bauxite and BFA based conventional castable with 15% cement
Water addition (%)
9.5
Flow (%) -ASTM C230 at 35°C
Initial flow
128 
At 30 minutes
115 
At 60 minutes
47 
Working time (minutes) at 35°C
After 20 seconds vibration
70 
Compressive strength (MPa)
After drying at 110°C for 24 hours
59 
After firing at 800°C for 6 hours
44 
After firing at 1100°C for 6 hours
26 
After firing at 1400°C for 6 hours
59 

News and events

Documentation

#

SECAR® Range

Global multi-references
for calcium aluminates

Please Note: You may have disabled JavaScript and/or CSS. Although this news content will be accessible, certain functionality is unavailable.

« Précédent

Suivant »


   © SECAR®    Site map    Legal notes    Recommended links    Refractory industries
Kerneos